the acrylated epoxy oligomer ( adgde) used for uv curing process was synthesized by the reaction of diethylene glycol diglycidyl ether with acrylic acid.

一缩二乙二醇二缩水甘油醚（DGDE）与丙烯酸为原料，合成紫外光固化环氧丙烯酸（ADGDE）齐聚物。

an experiment has been made to cure oligomer trihydroxy methyl propane tri acrylate ( tmpta) in sds-ii at ( 20 kv) and 2_c/ cm~ 2 dose.

在此基础上使用SDS-II型曝光机在20kV的加速电压、2μC/cm2的曝光剂量下，对经真空挥发处理过的三羟甲基丙烷三丙烯酸酯（TMPTA）液态低聚物进行了曝光试验，得到了固化结构。

dendritic acrylate oligomer with multiple acrylate double bond ( dao) was synthesized by michael addition reaction of ethylene diamine ( eda) and trimethylolpropane triacrylate ( tmpta) at 30 ℃ for 6 hours, using methanol as catalyst.

通过乙二胺（EDA）和三羟甲基丙烷三丙烯酸酯（TMPTA），以甲醇为催化剂，在30℃进行6小时Michael加成反应，可制得含多个双键的树枝状丙烯酸酯齐聚物（DAO）。